GRADIA® DIRECT Flo
Light-Cured, Flowable Microfilled Hybrid Composite Resin

GRADIA DIRECT Flo is a light-cured, highly flowable composite. Designed to be used in combination with GRADIA DIRECT, its physical properties, flow characteristics and direct application make this material ideal as a liner under composite restorations. GRADIA DIRECT Flo’s non-sticky formula shapes perfectly to cavity wall, making it easy to handle.
- Radiopaque
- Use as a sealant
- High polishability
- Use for tunnel preps
- Use as a liner or base
- High flow characteristics
- Use to block out undercuts
- Use to restore imperfections
- Flows easily for use as a liner or base
- Silica filled with average particle sizes of 0.7 microns
- A1, A2, A3, A3.5, A03 (Opaque Dentin), CV (Cervical Shade), BW (Bleach White)
- Flows quickly to place as a sealant when used with G-BOND™, the revolutionary one component, one coat, self-etch bonding agent
- Fluoro-alumino silicate glass fillers releases fluoride ions improving the resistance of teeth to acidic attack and prevents secondary decay
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
Contact GC America for contributing doctor’s information.
- Very low viscosity
- Filled composite resin
- Available in seven shades
- Fluoride (fluoro-alumino silicate glass filler)
IADR Abstract - Bond Strength of Repaired Filling Materials Using Different Repair Procedures
Description | |
3-Point Bending Strength (@ 24 hours) | 149 MPa (6) |
Consistency: 4 gf (@ 90 seconds) | 35.5 mm |
Depth of Cure | 3.7 mm |
Light-Cure | 20 seconds |
Radiopacity | Yes |
Solubility-Distilled Water | 1.5 µg/mm3 (0.2) |
Surface Hardness Strength (@ 24 hours) | 323 VHN: MPa (7) |
Surface Roughness | 0.16 µm |
Water Sorption | 24.7 µg/mm3 (0.4) |
Working Time under Dental Light | 1 minute, 10 seconds |
|
![]() |